interesting.

and yes it is overlooked very often and specifically at a retail level. I believe PDI have subtlety suggested in some announcements that the gold is free milling (images of gold in panning etc) however obviously that is open to interpretation without proper met test work. I would be surprised if it was refractory and if so will be a huge dent into the SP - I don't know if the current resource would justify the capex of a plant.

Interesting you say that re DEG, the last 12ish months I have held PDI I always have been very reiterating in previous PDI threads that metallurgical test work is a massive milestone and could be a potential value capper on MC too, and only a few have recognised and agreed. it always seems to be about assays assays assays on HC sometimes. I think that met work & sovereign risk factor/s also has a much bigger effect on MC than we have liked to recognise in the past.