worked well so far, the IP is good at getting you to the cloud of disseminated sulphides, which is the 0.2 to 1% combined cu/ni material, this stuff tells you have a fertile target and is even economic when bulked out over thick intervals. Ultimately would like to keep seeing more connected sulphides (semi massive to massive sulphides) which show up in tuw downhole EM and are modelled as plates, this is where the good gear lives around 2 to 10% combined cu/ni