There could be other problems tbh,
like for precast it’d need to:
-consistently improve the properties in question under real testing (not random side by side “comparisons”)

-not cause major workability problems (is certainly better than steel fibres but that isn’t hard)

-not cause any major problems with other concrete properties

-not cause major difficulties cleaning moulds, silicosis is an issue anyway but if it requires much more hardcore procedures/PPE that’s a problem

-not cause any kind of quality or durability issue - there is a potential problem with galvanic corrosion which may not be a real issue but IMHO hasn’t been satisfactorily explored enough to build stuff with a 100 year design life using CNT. The literature is contradictory and it’s a problem anyone marketing a CNT product would want/need to solve.